We can fully provide all the materials and accessories used in the production of aluminum ingot production and aluminum rod, including aluminum melting furnace equipment, launder, filter box, online degassing equipment, hot top casting, aluminum ingot casting production line, stacking ingot robot, dust removal equipment, ash stir-frying machine, ball mill, etc., out of the casting industry, the post-processing link of aluminum rod - aluminum profile extrusion, we can also provide products. Aluminum extruder, single rod heating furnace or multi-rod heating furnace, mold heating furnace, mold nitriding furnace, hydraulic oil cooler, cold bed, straightening machine, traction machine, online quenching, aging furnace, air compressor and other equipment, as well as graphite plate, mold, high temperature drum, ring belt, felt sleeve and other consumable materials. Billet Products, Aluminium Tube Extrusion, Aluminum Airfoil Extrusion, Aluminum casting process: The recycled aluminum scrap is to be heated and melted in an aluminum melting furnace,add with pure aluminum ingot, with refining flux and dross flux, the impurities will be removed, Then silicon and magnesium will be put into molten aluminum ,After flowing into launder and filter box,the molten aluminum finally reach the ingot casting line, with stacking robot, aluminum ingot will be stacked and packaging. While aluminium billet is another casting equipment, molten aluminum flows into Hot top casting plate, after cooling and Lifting and lowering of pallets, the billet will be made under the plate, then aluminum billet is hoisted out by the crane and enters the homogenization furnace, finally cut by saw.

Factory wholesale Extrusion Die Design - High quality Adc12 99.7 A7 A Grade Aluminum alloy Ingots – ZheLu Detail:

After all the charge is melted, stir well and take samples for analysis. Calculate the addition amount of fast-melting silicon according to the analysis results. When the molten aluminum reaches 740-770 °C (the process of adding silicon is an endothermic reaction, the temperature of the molten metal must be heated to keep the temperature not lower than 740 °C), throw the instant silicon agent on the molten aluminum surface for use, and press the bell into the molten aluminum. Stir in for 2-5 minutes. Product description: The silicon content is 95%, and it can be rapidly melted at low temperature, which greatly reduces the cost of alloy ingredients, and can quickly prepare any silicon-aluminum alloy with silicon content; the composition control is extremely precise, and a large number of inclusions and harmful substances that are easily brought into the master alloy are eliminated. Impurities, to avoid the use of waste miscellaneous aluminum to prepare aluminum-silicon master alloys and the impact on the quality of the final aluminum alloy that is difficult to control.

Product detail pictures:

Related Product Guide:

Our complete line solutions include: aluminum alloy ingot/Billet production line and aluminum extrusion production line. Factory wholesale Extrusion Die Design - High quality Adc12 99.7 A7 A Grade Aluminum alloy Ingots – ZheLu , The product will supply to all over the world, such as: Sri Lanka, South Africa, Hongkong, Foshan Zhelu has successfully developed 6 series aluminum alloy profile products with high strength and high corrosion resistance, which can be used in ships and other fields.

Alunimun Extrusion Press Line

Colouring Agent

Exatech Inc

Extrusion Die Manufacturer

Foil Wrappers For Chocolate Bars

Homogenizing Process

Hydraulic Valve

Insulation Anchors

Metal Extrusion Machine

Metal Furnace Door

The company can think what our think, the urgency of urgency to act in the interests of our position, can be said this is a responsible company, we had a happy cooperation!